Disclosed is a method for preparing a graphene/silver/titanium dioxide composite. The method comprises: (1) weighing graphene sheets (2) dispersing the graphene sheets weighed in step (1) into an aqueous solution into which a suitable amount of a surfactant (PVP or SDS) is added, and performing ultrasonic dispersion (3) adding silver nitrate in a calculated amount into the graphene sheet solution treated in step (2), then maintaining a temperature in an oil bath pan, and dropwise adding a reducing agent (N2H4, NaBH4 or vitamin C and the like) in a corresponding calculated amount, and after maintaining the temperature for a certain amount of time, obtaining a graphene/silver composite solution and (4) after heating the graphene/silver composite solution prepared in step (3) to another temperature and maintaining the temperature for a certain amount of time, slowly adding a solution of a chloride salt of titanium (TiCl3 or TiCl4) in a calculated amount, and after performing suction filtration, washing and vacuum drying treatments, obtaining a graphene/silver/titanium dioxide composite powder. The method is simple in preparation process and easy to popularize and apply.Linvention concerne un procédé de préparation de composite de graphène/argent/dioxyde de titane. Le procédé comprend les étapes suivantes : (1) peser des feuilles de graphène (2) disperser les feuilles de graphène pesées dans létape (1) dans une solution aqueuse dans laquelle une quantité appropriée de tensioactif (PVP ou SDS) est ajoutée, et effectuer une dispersion par ultrasons (3) ajouter une quantité calculée de nitrate dargent dans la solution de feuilles de graphène traitée dans létape (2), puis maintenir une température dans une cuve à bain dhuile, et ajouter goutte à goutte une quantité calculée correspondante dun agent réducteur (N2H4, NaBH4 ou de la vitamine C ou un agent similaire), et après avoir maintenu la température pendant un certain laps de temps, obtenir une solution de composite de