A thermoplastic elastomer stopper that meets the desired material properties of a stopper for a syringe assembly is disclosed. The compression set of the thermoplastic elastomer stopper of the present disclosure is ≤50% when measured at 25% compression for 22 hrs at 70 degree C. The hardness of the thermoplastic elastomer stopper of the present disclosure is 40-70 Shore A. The viscosity of a thermoplastic elastomer stopper of the present disclosure is ≥70 Pa·s at 1,000 s−1 shear rate, ≥12.0 Pa·s at 10,000 s−1 shear rate, and ≥3.0 Pa·s at 50,000 s−1 shear rate when measured using a capillary rheometer at 205 degree C. (Die: Roundhole 20 mm length/1 mm diameter/180 degree inlet, Piston: d=15 mm, and melting time=7 min). The present non-lubricated stopper exhibits the required functional performance of a lubricated stopper.La présente invention concerne un bouchon en élastomère thermoplastique qui satisfait à des propriétés souhaitées en termes de matériaux d'un bouchon destiné à un ensemble seringue. La déformation rémanente à la compression du bouchon en élastomère thermoplastique de la présente invention est ≤ 50 % lorsque celle-ci est mesurée à 25 % de compression pendant 22 h à 70 °C. La dureté du bouchon en élastomère thermoplastique de la présente invention est située dans la plage allant de 40 à 70 Shore A. La viscosité d'un bouchon en élastomère thermoplastique de la présente invention est ≥ 70 Pa.s à une vitesse de cisaillement de 1 000 s-1, ≥ 12,0 Pa.s à une vitesse de cisaillement de 10 000 s-1, et ≥ 3,0 Pa.s à une vitesse de cisaillement de 50 000 s-1 lorsque celle-ci est mesurée à l'aide d'un rhéomètre capillaire à 205 °C (matrice : orifice rond 20 mm de longueur / 1 mm de diamètre / entrée à 180 degrés ； piston : d = 15 mm, et temps de fusion = 7 min). Le bouchon non lubrifié selon la présente invention présente les performances fonctionnelles requises d'un bouchon lubrifié.