Provided is an absorbent resin capable of enhancing the diffusibility of a liquid to be absorbed and effectively reducing the amount of backwash. The water absorbent resin according to the present invention is a water absorbent resin obtained by polymerizing a water-soluble ethylenically unsaturated monomer in the presence of an internal cross-linking agent, wherein the absorbing ability of physiological saline under a load of 4.14 kPa is 20 ml / g or more after 120 minutes from the start of absorption, When the swelling degree is assumed to be 100% under a load of 4.14 kPa after 120 minutes, the swelling degree under load is 70% or less after 30 minutes. Such a water absorbent resin includes a step of carrying out polymerization in the presence of an azo compound and a peroxide in a method of producing a water absorbent resin by reversely suspension-polymerizing a water-soluble ethylenically unsaturated monomer in a hydrocarbon dispersion medium in the presence of an internal cross- And a step of post-crosslinking the hydrogel obtained by polymerization with a post-crosslinking agent.피흡수액의 확산성을 높이고, 역류량을 효과적으로 저감시킬 수 있는 흡수성수지를 제공한다.본 발명에 따른 흡수성수지는, 수용성 에틸렌성 불포화 단량체를 내부 가교제 존재하에서 중합시킴으로써 얻어지는 흡수성수지로서, 4.14kPa 하중하에서의 생리식염수의 흡수능이 흡수 개시로부터 120분 경과후에 20ml/g 이상이고, 흡수 개시로부터 120분 경과후의 4.14kPa 하중하에서의 생리식염수의 흡수능을 하중하 팽윤도 100%라 했을 때, 30분 경과후에 하중하 팽윤도가 70% 이하이다. 이러한 흡수성수지는, 수용성 에틸렌성 불포화 단량체를 탄화수소 분산매중에서, 내부 가교제의 존재하, 역상현탁중합시켜 흡수성수지를 제조하는 방법에 있어서, 아조계 화합물과 과산화물의 존재하에서 중합을 실시하는 공정과, 이러한 중합으로 얻은 함수 겔상물을 후가교제로 후가교 하는 공정, 에 의해 제조할 수 있다.