Problem to be solved: to provide a glass article having low friction coating and low friction coating.In accordance with one embodiment, the coated glass article preferably comprises a glass body and a low friction coating positioned at least in part of the first surface of the glass body.The low friction coating may include a polymer chemical composition.The coated glass article can be thermally stable for 30 minutes at a temperature of at least about 260 degrees Celsius.The light transmittance of coated glass articles is preferably about 55% or more of the light transmittance through uncoated glass articles pertaining to wavelengths between about 400 nm and about 700 nm.The low friction coating may have a mass loss rate of less than about 5% of the mass, when heated to a temperature of 150C to 350.degree. C. at a temperature rise rate of about 10.degree. C. / min.Diagram【課題】低摩擦コーティングおよび低摩擦コーティングを備えるガラス製物品を提供する。【解決手段】一実施形態によれば、コーティングされたガラス製物品は、第１の表面をガラス本体と、ガラス本体の第１の表面の少なくとも一部分に位置された低摩擦コーティングとを備えていることが好ましい。低摩擦コーティングは、ポリマー化学組成物を含んでいてもよい。コーティングされたガラス製物品は、少なくとも約２６０℃の温度で３０分間の間熱的に安定し得る。コーティングされたガラス製物品の光透過率は、約４００ｎｍ～約７００ｎｍの波長に係るコーティングされていないガラス製物品を通した光透過率の約５５％以上であることが好ましい。低摩擦コーティングは、約１０℃／分の昇温速度で１５０℃から３５０℃の温度に加熱された場合、その質量の約５％未満の質量損失率を有し得る。【選択図】図１