I discloses a method of making a composite material embedded in a matrix is non-spherical reinforcing particles. In the present method, in a first step, is bound to the non-spherical reinforcing particles superparamagnetic nanoparticles and / or magnetic, in the second step, a liquid matrix precursor and liquid matrix material and / or reinforcing particles obtained are introduced to the body material, in the third step, and / or crosslinking and / or polymerization and solidification of the matrix material. In the present invention, applying a magnetic field before and / or during the cross-linking and / or polymerization and solidification of the matrix precursor material or matrix material and / or each reinforcing particles to orient in the matrix, the third during and after the process, fixed in the matrix in this orientation, the length of the 1-D (l) is at least 0.5μm, preferably, non-spherical reinforcing particles, nano-particles to non-spherical reinforcing particles weight ratio is less than 0.25.非球状強化用粒子がマトリックスに埋め込まれた複合材料を作製する方法を開示する。本方法では、第1の工程において、磁性および/または超常磁性ナノ粒子を非球状強化用粒子に結合させ、第2の工程において、得られた強化用粒子を液体マトリックス材料および/または液体マトリックス前駆体材料に導入し、第3の工程において、マトリックスの材料を固化および/または重合および/または架橋する。本発明において、それぞれマトリックス材料またはマトリックス前駆体材料の固化および/または重合および/または架橋の前および/または最中に、マトリックス中で強化用粒子が配向するように磁場を印加し、第3の工程の最中および後に、この配向をマトリックス中で固定し、非球状強化用粒子は、好ましくは1次元の長さ(l)が少なくとも0.5μmであり、非球状強化用粒子に対するナノ粒子の重量比が、0.25未満である。