FIELD: chemistry.SUBSTANCE: foam material is made from the composition, containing the polyolefin dispersion with the high crystalline degree, the crosslinked binder and the surfactant. The foamed polymeric cellular material is produced by mechanical mixing with the composition air, containing the polyolefin dispersion with the high crystalline degree, the binder and the surfactant, capable to crosslinking. The resulting foam is dried at the temperature below the foam material melting point and above the binder crosslinking temperature. In the production of the cellular material, the composition additionally contains the fibers, non-swelling particles, or combinations thereof.EFFECT: production of foamed cellular material with open pores and with improved mechanical strength.10 cl, 8 dwg, 3 tblИзобретение относится к вспененному полимерному пеноматериалу с открытыми порами и к способу его получения. Пеноматериал выполнен из композиции, содержащей дисперсию полиолефина с высокой степенью кристалличности, сшитое связующее и поверхностно-активное средство. Вспененный полимерный пеноматериал получают механическим смешиванием с воздухом композиции, содержащей дисперсию полиолефина с высокой степенью кристалличности, способное к сшиванию связующее и поверхностно-активное средство. Образовавшуюся пену высушивают при температуре ниже температуры плавления пеноматериала и выше температуры сшивания связующего. При получении пеноматериала композиция дополнительно содержит волокна, ненабухающие частицы или их комбинации. Изобретение обеспечивает получение вспененного пеноматериала с открытыми порами с улучшенной механической прочностью. 2 н. и 8 з.п. ф-лы, 8 ил., 3 табл.