The present invention relates to a method for preparing a three-dimensional polymer scaffold (3D-PS) for use in tissue-engineering, said method comprising the subsequent steps of a) providing a polymeric precursor scaffold (p-PS) comprising at least one biodegradable natural polymer (P A ) ； b) treating the polymeric precursor scaffold (p-PS) with a cross-linking agent comprising glutaraldehyde to induce cross-linking of the natural polymer (P A ), thereby forming a cross-linked polymer scaffold (x-PS)； c) subjecting the cross-linked polymer scaffold (x-PS) of step b) to low-pressure plasma treatment involving exposure of the polymer scaffold to an ionized oxygen-containing gas plasma at a pressure in the range of 10 -3 to 10 -6 bar and a temperature below 40°C.La présente invention concerne un procédé de préparation d'un échafaudage polymère tridimensionnel (3D-PS) destiné à être utilisé en génie tissulaire, ledit procédé comprenant les étapes consistant à a) fournir un échafaudage précurseur polymère (p-PS) comprenant au moins un polymère naturel biodégradable (PA) ； b) traiter l'échafaudage précurseur polymère (p-PS) avec un agent de réticulation comprenant du glutaraldéhyde afin d'induire la réticulation du polymère naturel (PA), formant ainsi un échafaudage polymère réticulé (x-PS) ； c) soumettre l' échafaudage polymère réticulé (x-PS) de l'étape b) à un traitement plasma à basse pression impliquant l'exposition de l'échafaudage polymère à un plasma de gaz contenant de l'oxygène ionisé à une pression dans la plage de 10-3 à 10-6 bars et à une température inférieure à 40 °C.