An implant having a three-dimensional structure based on an alloy and such an alloy is disclosed. The alloy comprises a single phase MgZn alloy containing 2.0 wt% Zn to 6 wt% Zn and having less than 0.001 wt% of one or more other elements and the balance Mg. In some embodiments, the alloy is substantially free of microgalvanic elements. In some embodiments, the alloy contains a less valuable nano-sized precipitate than the Mg matrix alloy, and has a Zn content ranging from 3.0 wt% Zn to 6 wt% Zn and a calcium content ranging from 0.0005 wt% to 1.0 wt% And less than 0.001% by weight of one or more other elements, with the balance Mg being MgZnCa alloy. In another embodiment, the alloy contains a less precious nano-sized precipitate (the nano-sized precipitate is more valuable than the Mg matrix) than the Mg matrix alloy, and contains Zn in the range of 3.0 wt% Zn to 6 wt% Zn , A Mg content in the range of 0.0005 wt.% To 1.0 wt.%, And less than 0.001 wt.% Of one or more other elements and the balance Mg.합금 및 그러한 합금을 기반으로 하는, 3차원 구조를 갖는 임플란트가 개시된다. 합금은 2.0 중량%의 Zn 내지 6 중량%의 Zn을 함유하고, 0.001 중량% 미만의 하나 이상의 기타 원소들을 갖고, 잔부가 Mg인 단일상 MgZn 합금을 포함한다. 일부 실시 형태에서, 합금에는 마이크로갈바닉(microgalvanic) 원소가 실질적으로 부재한다. 일부 실시 형태에서, 합금은 Mg 매트릭스 합금보다 덜 귀한 나노크기의 침전물을 함유하며, 3.0 중량%의 Zn 내지 6 중량%의 Zn의 범위의 Zn 함량 및 0.0005 중량% 내지 1.0 중량%의 범위의 칼슘 함량을 갖고, 0.001 중량% 미만의 하나 이상의 기타 원소들을 갖고, 잔부가 Mg인 MgZnCa 합금을 포함한다. 다른 실시 형태에서, 합금은 Mg 매트릭스 합금보다 덜 귀한 나노크기의 침전물 (복수의 나노크기의 침전물은 Mg 매트릭스보다 더 귀함)을 함유하며, 3.0 중량%의 Zn 내지 6 중량%의 Zn의 범위의 Zn 함량, 0.0005 중량% 내지 1.0 중량%의 범위의 칼슘 함량을 갖고, 0.001 중량% 미만의 하나 이상의 기타 원소들을 갖고, 잔부가 Mg인 MgZnCa 합금을 포함한다.