[Problem] To provide a chlorine dioxide agent which is obtained by impregnating a porous support with a chlorite and subsequently drying the resulting material, and which stably generates chlorine dioxide at a high concentration. [Solution] A neutral to weak alkaline calcined sepiolite that has a pH of 7 or more but less than 10 is used as a porous support for a chlorine dioxide agent. In addition, the calcined sepiolite has a calcium content of less than 5% by weight. A chlorine dioxide agent according to the present invention is characterized by being obtained by impregnating this calcined sepiolite with a chlorite and subsequently drying the resulting material. This chlorine dioxide agent is characterized by stably generating chlorine dioxide at a high concentration.Le problème décrit par la présente invention est de fournir un agent de dioxyde de chlore qui est obtenu par imprégnation d'un support poreux avec un chlorite et par séchage ultérieur du matériau résultant, et qui génère de manière stable du dioxyde de chlore à une concentration élevée. Une sépiolite calcinée neutre à faiblement alcaline, qui a un pH supérieur ou égal à 7 mais inférieur à 10, est utilisée en tant que support poreux pour un agent de dioxyde de chlore. De plus, la sépiolite calcinée a une teneur en calcium inférieure à 5 % en poids. Un agent de dioxyde de chlore selon la présente invention est caractérisé en ce qu'il est obtenu par imprégnation de cette sépiolite calcinée avec un chlorite et par séchage ultérieur du matériau résultant. Cet agent de dioxyde de chlore est caractérisé par la génération stable de dioxyde de chlore à une concentration élevée.【課題】多孔質担体に亜塩素酸塩を含浸し、乾燥させて得られる二酸化塩素剤で、高濃度の二酸化塩素を安定して発生する二酸化塩素剤を提供する。 【解決手段】二酸化塩素剤の多孔質担体として、ｐＨ７以上且つｐＨ１０未満の中性～弱アルカリ性の焼成セピオライトを使用する。またその焼成セピオライトはカルシウム含有量が５重量％未満である。この焼成セピオライトに亜塩素酸塩を含浸し、乾燥させることを特徴とする二酸化塩素剤である。この二酸化塩素剤は、高濃度の二酸化塩素を安定して発生する特徴を有している。