The present invention relates to a method for manufacturing granular-type bed soil by using zeolite and diatomite. According to the present invention, the method for manufacturing granular-type bed soil for covering soil and granular-type bed soil for a seedbed comprises: a mixed material generating step of generating a mixed material by mixing zeolite, having a particle size of 3 mm or smaller and pH 6.0-8.0, and diatomite having a particle size of 3 mm or smaller and pH 3.5-4.5； a granular-type bed soil manufacturing step of manufacturing granular-type bed soil, having a particle size of 0.1-8 mm and pH 4.5-6.0, by inserting the mixed material and nutrient liquid in a pan assembler； a coating and hot-air drying step of simultaneously performing zeolite coating treatment on a surface of the granular-type bed soil by using zeolite powder and hot-air drying of the granular-type bed soil； and a particle size separation step of separating the granular-type bed soil for which the zeolite surface coating and the hot-air drying have been performed into granular-type bed soil, having a particle size of 1-2.5 mm, for covering soil and granular-type bed soil, having a particle size of 2.5-5.5 mm, for a seedbed.본 발명은 제올라이트와 규조토를 이용한 입상형 상토를 제조하는 방법에 관한 것이다. 본 발명의 일 실시예에 따른 복토용 입상형 상토와 모판용 입상형 상토의 제조방법은 입도가 3mm 이하이고 pH가 6.0~8.0인 제올라이트(zeolite)와 입도가 3mm 이하이고 pH가 3.5~4.5인 규조토를 혼합하여 혼합원료를 생성하는 혼합원료 생성단계와, 팬조립기에 혼합원료와 양액을 투입하여 입도가 0.1~8mm이고 pH가 4.5~6.0인 입상형 상토를 제조하는 입상형 상토 제조 단계와, 제올라이트 파우더를 이용한 입상형 상토의 표면의 제올라이트 코팅 처리와 입상형 상토의 열풍 건조를 함께 수행하는 코팅 및 열풍 건조 단계와, 제올라이트 표면 코팅 및 열풍 건조가 수행된 입상형 상토를 입도가 1~2.5mm인 복토용 입상형 상토와 입도가 2.5~5.5mm인 모판용 입상형 상토로 분리하는 입도 분리 단계를 갖는다.