According to the present invention, provided is an integrated multi-layered insulation curtain having both water repellency and exothermicity. For the above, the disclosed multi-layered insulation curtain disclosed by the present invention is made by: insolubilizing fiber obtained by melting and spinning polycarbosilane, and polyester staple fiber having a carbon nanocomposite coating layer and a silicon coating layer formed on the surface thereof, mixing silicon carbide staple fiber thermally treated at 1,300-1,400°C at a weight ratio of 80:20 to 50:50, and carding the same to form a web； putting an insulating material for padding formed by performing a needle punching thereof into a space between an outer cover and an inner cover formed respectively with any one between polyethylene terephthalate and polyprolylen； and thermally fusing the outer cover, the insulation material, and the inner cover at intervals.본 발명은 발수성과 발열성을 동시에 갖는 융합형 다겹 보온커튼을 제공하기 위한 것이다.이를 위해 본 발명에서는 표면에 실리콘 코팅층과 탄소나노복합체 코팅층이 형성된 폴리에스테르 단섬유와, 폴리카보실란을 용융 방사해서 얻은 섬유를 불용화한 후 1300~1400℃에서 열처리한 실리콘 카바이드 단섬유를 80:20 내지 50:50의 중량비로 혼섬한 후 카딩하여 웹을 형성하고, 이를 니들펀칭하여 형성된 패딩(padding)용 보온재를 폴리에틸렌 테레프타레이트(Polyethylene terephthalate)나 폴리프로필렌(Polypropylen) 중 어느 하나로 각각 이루어진 겉감과 안감 사이에 넣고, 상기 겉감과 상기 보온재 및 상기 안감을 일정한 간격을 두고 열융착하여 형성된 다겹 보온커튼을 개시한다.