The present invention relates to an absorbent article containing a particulate superabsorbent polymer composition having improved stability comprising a polymer comprising from about 0.01wt% to about 5wt% of a neutralized aluminum salt solution applied to the surface of a particulate superabsorbent polymer wherein an 5 aqueous solution of the neutralized aluminum salt has a pH value from about 5.5 to about 8 and the particulate superabsorbent polymer composition has a mean particle size distribution of from 300 to 400µm, an original Free Swell Gel Bed Permeability (FSGBP) of about 20x10-8 cm2 to about 200 x10-8 cm2 and a compressibility of from about 1.30mm2/N to about 4mm2/N and the particulate superabsorbent polymer 10 composition has a permeability stability index of from about 0.60 to about 0.99 and having particles having a particle diameter of larger than 600µm in an amount of less than about 15wt% of the particulate superabsorbent polymer composition.La présente invention concerne un article absorbant contenant une composition polymère superabsorbante particulaire présentant une stabilité améliorée comprenant un polymère comprenant denviron 0,01 % en poids à environ 5 % en poids dune solution de sel daluminium neutralisé appliquée à la surface du polymère superabsorbant particulaire une solution aqueuse du sel daluminium neutralisé présentant une valeur de pH denviron 5,5 à environ 8 et la composition polymère superabsorbante particulaire présentant une distribution moyenne des tailles de particule de 300 à 400 µm, une perméabilité initiale de lit de gel à gonflement libre (FSGBP) denviron 20 x 10-8 à environ 200 x 10-8 cm² et une compressibilité denviron 1,30 mm²/N à environ 4 mm²/N et la composition polymère superabsorbante particulaire présentant un indice de stabilité de la perméabilité denviron 0,60 à environ 0,99 et présentant des particules dotées dun diamètre de particule supérieur à 600 µm en une quantité inférieure à environ 15 % en poids de la co