The present invention is a curable composition for producing a dental composite crown, which comprises a polymerizable (meth)acrylate not containing a urethane moiety and a polymerizable urethane (meth)acrylate, and does not contain a urethane moiety. Fumed silica in an amount of less than 8% by weight, based on the weight of the resin matrix, the nanoclusters and the total composition, in which the polymerizable (meth)acrylate is used in excess over the polymerizable urethane (meth)acrylate. And a photoinitiator, an organic dye, and an initiator system comprising a photoinitiator, an organic dye, the curable composition comprising no more than 5% by weight, based on the weight of the total composition, of a softener. Curable composition relates to a curable composition having a viscosity of less than 150 Pa * s at 23° C. and a shear rate of 1 s −1 . The present invention also relates to a cured article obtained by radiation curing this curable composition using the additive manufacturing method.本発明は、歯科用コンポジットクラウンを製造するための硬化性組成物であって、ウレタン部分を含まない重合性（メタ）アクリレート、及び、重合性ウレタン（メタ）アクリレートを含み、ウレタン部分を含まない重合性（メタ）アクリレートが、重合性ウレタン（メタ）アクリレートよりも過剰に使用されている、樹脂マトリックスと、ナノクラスター及び、全組成物の重量に対して８重量％未満の量のヒュームドシリカを含む充填剤マトリックスと、光開始剤、有機染料、を含む開始剤系とを含み、硬化性組成物は、全組成物の重量に対して５重量％を超える量の軟化剤を含まず、硬化性組成物は、２３℃及び１ｓ－１の剪断速度において１５０Ｐａ＊ｓ未満の粘度を有する、硬化性組成物に関する。本発明はまた、積層造形方法を使用して、この硬化性組成物を放射線硬化させて得られる硬化物品にも関する。