Calcite
专利权人:
東ソー株式会社
发明人:
畦地 翔,伊藤 晶子,船越 肇,藤崎 浩之
申请号:
JP2019072536
公开号:
JP2020169155A
申请日:
2019.04.05
申请国别(地区):
JP
年份:
2020
代理人:
摘要:
SubjectEven in the case of a shortened sintering method, at least one of the calcination material and the method for producing the sintered body having a light permeable property capable of being permitted as a dental prosthesis can be obtained.SolutionContains zirconia containing stabilizerThe measured density was 3.15 g / cm. Sup. 3 or more and 4.30 g / cm. Sup. 3 or less..In the airTemperature rise rate: 600 ℃ / hourMaximum reach temperatureFor the crystallite diameter after the treatment time was maintained for 1 hour and the temperature at 600 ℃ / h of the heating temperature.In the airTemperature rise rate: 600 ℃ / hourMaximum reach temperatureThe ratio of the crystallite diameter after processing with the firing program for 1 hour and the temperature reduction rate of 600 ° C. / hour is less than 110% and not more than 150Calcite characterized byNo selection【課題】 短縮された焼結方法であっても、歯科用補綴物として許容され得る透光性を有する焼結体が得られる仮焼体及びその製造方法の少なくともいずれかを提供する。【解決手段】 安定化剤を含有するジルコニアを含み、実測密度が3.15g/cm3以上4.30g/cm3以下であり、なおかつ、大気中、昇温速度600℃/時間、最高到達温度1300℃、保持時間1時間及び降温速度600℃/時間の焼成プログラムで処理した後の結晶子径に対する、大気中、昇温速度600℃/時間、最高到達温度1300℃、保持時間1時間及び降温速度600℃/時間の焼成プログラムで処理した後の結晶子径の割合が110%以上150℃以下であること、を特徴とする仮焼体。【選択図】なし
来源网站:
中国工程科技知识中心
来源网址:
http://www.ckcest.cn/home/

意 见 箱

匿名:登录

个人用户登录

找回密码

第三方账号登录

忘记密码

个人用户注册

必须为有效邮箱
6~16位数字与字母组合
6~16位数字与字母组合
请输入正确的手机号码

信息补充