摘要：
PROBLEM TO BE SOLVED: To provide a chemically resistant glass suitable as pharmaceutical package, bottle, syringe, carpoule or ampoule and as a chemically pre-stressed glass, and a method of its use.SOLUTION: There is provided a glass comprising the following components given in mol% on oxide basis: SiO: 64-77, AlO: 5-14, NaO: 4-12, CaO: 1-12, MgO: 0-14, ZrO: 0-2, and TiO: 0-4.5, wherein the ratio AlO/NaO is 1 or more and the ratio AlO/CaO is 1.5 or more, and the total content SiO+AlOis less than 82 mol%, being chemically pre-stressed by means of ion-exchange, having a working temperature T4 of less than 1350°C, and having the hydrolytic resistance according to HGB1(DIN-ISO-719) and HGA(DIN-ISO-720).SELECTED DRAWING: None【課題】医薬品包装、びん、シリンジ、カートリッジ又はアンプルとして及び化学強化ガラスとして適した化学的に安定なガラス及びその使用方法の提供【解決手段】酸化物をベースとしてモル％で以下の成分：ＳｉＯ2：６４～７７、Ａｌ2Ｏ3：５～１４、Ｎａ2Ｏ：４～１２、ＣａＯ：１～１２、ＭｇＯ：０～１４、ＺｒＯ2：０～２、ＴｉＯ2：０～４．５を含有し、ここで、Ａｌ2Ｏ3／Ｎａ2Ｏの比が１以上であり、かつＡｌ2Ｏ3／ＣａＯの比が１．５以上であり、ＳｉＯ2＋Ａｌ2Ｏ3の総含有率が８２モル％未満であるイオン交換により化学強化されたガラスであり、１３５０℃未満の加工温度Ｔ４、ＨＧＢ１（ＤＩＮ－ＩＳＯ－７１９）及びＨＧＡ（ＤＩＮ－ＩＳＯ－７２０）に従った加水分解安定性を有するガラス。【選択図】なし