PURPOSE: A titanium based alloy including titanium-niobium-tantalum is provided to have an excellent resistance to an oxidation condition and a temperature formed in a plastic process when an implant is manufactured, thereby maximally preventing the generation of a surface oxide layer. CONSTITUTION: A titanium based alloy comprises 10-15 atom% of niobium, 10-15 atom% of tantalum and the rest of titanium and the other unavoidable impurities. In the titanium based alloy, a content of niobium is 13 atom%. A dental implant including the titanium based alloy comprises: a fixture which is fixed at an alveolar bone； a crown which forms the exterior of the dental implant； and an abutment in which one end is connected with the crown and the other end is connected with the fixture. The abutment supports the crown and comprises 10-15 atom% of niobium, 10-15 atom% of tantalum and the rest of titanium and the other unavoidable impurities. [Reference numerals] (AA) Evaluation of degree of oxidation layer generation after heat-treating at 800°；C； (BB) Before heat-treating； (CC) After heat-treating내산화성이 우수한 티타늄계 합금을 개시한다. 이 티타늄계 합금은 니오브: 12~15 원자%, 탄탈: 12~15 원자%와 잔부의 티타늄 및 기타 불순물을 포함한다. 이 티타늄계 합금은 치과용 임플란트의 지대주로 쓰일 수 있다. 아울러 치과용 임플란트의 제조 방법을 개시한다. 이 방법은 고정체에 한쪽 끝이 연결된, 상기 티타늄계 합금 소재의 지대주의 반대쪽 끝에 상기 임플란트의 치관을 형성할 도재 전구체를 도포하는 단계, 상기 도재 전구체를 소성하여 도재 소재의 치관을 형성하는 단계 및 선택적인 단계로서, 상기 지대주의 표면을 질산과 불산의 수용액으로 세척하는 단계를 포함한다. 이 방법을 이용하여 우회 공정 없이 도재 치관을 직접 티타늄계 합금 소재의 지대주 위에 직접 설치할 수 있다. 또한 소성 공정으로 생길 수 있는 표면 산화막을 상기 질산과 불산의 수용액으로 세척할 수 있다.