The invention relates to a process of producing a dental zirconia article, the process comprising the step of sintering a porous dental zirconia article, the sintering comprising a heat-treatment segment A characterized by a heating rate of at least 3 K/sec up to a temperature of at least 1,200°C, the porous dental zirconia article being composed of a zirconia material containing 6.0 to 8.0 wt.% yttria, 0.05 to 0.12 wt.% alumina and comprising a coloring component containing Tb, the porous dental zirconia article being essentially free of Fe components. The invention also relates to a process comprising the additional step of applying a glazing composition to the outer surface of the porous zirconia article before the heat-treatment or sintering is conducted.L'invention concerne un procédé de production d'un article en zircone dentaire, le procédé comprenant l'étape de frittage d'un article en zircone dentaire poreux, le frittage comprenant un segment de traitement thermique A caractérisé par une vitesse de chauffage d'au moins 3 K/sec jusqu'à une température d'au moins 1 200 °C, l'article de zircone dentaire poreux étant composé d'un matériau de zircone contenant de 6,0 à 8,0 % en poids d'oxyde d'yttrium, de 0,05 à 0,12 % en poids d'alumine et comprenant un composant colorant contenant Tb, l'article de zircone dentaire poreux étant essentiellement exempt de composants Fe. L'invention concerne également un procédé comprenant l'étape supplémentaire consistant à appliquer une composition de vitrage sur la surface extérieure de l'article en zircone poreux avant la réalisation du traitement thermique ou du frittage.