The present invention relates to a method of forming a coated particle comprising with heating at a constant average temperature of about 40 ℃ the step of shaking the predetermined volume of the core particles. When the particles are generally uniformly mixed with no apparent agglomeration, vinyl-combines a premix under a mixed-functional silicone polymer, a hydride-functional crosslinking agent and a metal catalyst, a continuous propeller. Then, at a rate which ensures that upset grouping or aggregation of the fine particles, a vinyl-functional silicone polymer, a hydride-screen and siphon to the main vessel containing the core particles, heating the functional cross-linking agent and metal catalyst premix. When a uniform coating is achieved, heating the primary vessel to an average temperature of about 80 ℃ then it cooled again to room temperature (about 20 ℃ -28 ℃). Then, by passing the coated material to 45㎛ sieve to remove any large particles that may be present.본 발명은 약 40℃의 일정한 평균 온도로 가열하면서 소정 부피의 코어 입자를 진탕시키는 단계를 포함하는, 코팅된 입자를 형성하는 방법에 관한 것이다. 입자가 명백한 응집화없이 전반적으로 균일하게 혼합되면, 비닐-관능성 실리콘 중합체, 수소화물-관능성 가교제 및 금속 촉매를 연속적인 프로펠러-혼합하에 프리믹스로 조합한다. 이어서, 미립자의 군집화 또는 응집화가 없도록 보장하는 속도에서, 비닐-관능성 실리콘 중합체, 수소화물-관능성 가교제 및 금속 촉매 프리믹스를 가열된 코어 입자를 함유하는 주 용기로 사이펀화한다. 균일한 코팅이 달성되면, 주 용기를 약 80℃의 평균 온도로 가열한 다음, 실온 (약 20℃-28℃)으로 다시 냉각시킨다. 이어서, 코팅된 물질을 45㎛ 체에 통과시켜, 존재할 수 있는 임의의 큰 미립자를 제거한다.