The invention relates to: - A resilient resorbable chemically crosslinked collagen sponge for promoting soft tissue volume augmentation in the oral region, comprising 60-96 % (w/w) collagen and 4-40 % (w/w) elastin, which shows by mercury intrusion porosimetry interconnected pores with a median pore diameter between 50 and 90 µm and at least 80 % porosity with a pore diameter more than 10 µm, an onset temperature of 45 to 57 °C and a density in dry state from 50 to 65 mg/cm 3 . - A process for preparing that resilient resorbable chemically crosslinked collagen sponge, and - That resilient resorbable chemically crosslinked collagen sponge for use as an implant in the oral cavity for soft tissue volume augmentationLa présente invention concerne : - une éponge de collagène résorbable élastique réticulée chimiquement pour favoriser l'augmentation du volume des tissus mous dans la région buccale, comprenant 60 à 96 % en masse de collagène et 4 à 40 % en masse d'élastine, qui présente par porosimétrie par intrusion de mercure des pores interconnectés avec un diamètre médian des pores compris entre 50 et 90 μm et au moins 80 % de porosité avec un diamètre des pores supérieur à 10 μm ； une température de début de 45 à 57 °C et une densité à l'état sec de 50 à 65 mg/cm3. - Un procédé permettant de préparer ladite éponge de collagène résorbable élastique réticulée chimiquement, et - ladite éponge de collagène résorbable élastique réticulée chimiquement destinée à être utilisée en tant qu'implant dans la cavité orale pour l'augmentation du volume des tissus mous.