An object of the present invention is to provide a dental member having high strength, low elasticity and excellent engraftment stability after embedding, by preventing damage to the root at the time of embedding by miniaturization. Dental member for the formula: Zr a Ni b Cu c Al d [expression of a, b, c, d are, in atomic%, a is 60-75 atomic%, b is 11 to 30 atomic%, c is 1 to 16 Wherein the screw part is made of an amorphous alloy having a composition of 0.5 to 1.0 mm or a screw part having a length of 2 to 5 mm, Or a one piece type dental implant having a maximum diameter of 0.5 to 2.9 mm and a length of 2 to 13.4 mm of the thread portion or a dental implant having a maximum diameter of 0.5 to 2.9 mm And is used as a two piece type dental implant having a screw portion length of 2 to 5.9 mm.본 발명은 소형화에 의해 매립 때의 치근의 손상을 방지하고, 고강도 또한 저탄성이고 매립 후의 생착 안정성이 뛰어난 치과용 부재를 제공하는 것이다. 치과용 부재는 식 ： ZraNibCucAld［식 중의 a, b, c, d는 원자%로, a는 60 내지 75원자%, b는 11 내지 30원자%, c는 1 내지 16원자%, d는 5 내지 20원자%］로 나타나는 조성을 가지는 아모퍼스 합금에 의해 제조되고, 나사 부분의 곡경이 0.5㎜ 내지 1.0㎜ 또는 나사 부분의 길이가 2㎜ 내지 5㎜인 치과 교정용 앵커 스크류로서 이용되거나, 혹은 나사 부분의 최대 직경이 0.5 내지 2.9㎜ 및 나사 부분의 길이가 2 내지 13.4㎜인 원피스 형태(one piece type)의 치과용 임플란트이나, 나사 부분의 최대 직경이 0.5 내지 2.9㎜ 및 나사 부분의 길이가 2 내지 5.9㎜인 투피스 형태(two piece type)의 치과용 임플란트로서 이용된다.