FIELD: medicine.SUBSTANCE: present invention relates to lubricating coating (5) for medical injection device (1) comprising successively: bottom layer (50) in contact with surface (21) of container of medical device, which is necessary to provide lubrication, comprising a mixture of crosslinked and not cross-linked polydimethylsiloxane, intermediate layer (51) consisting essentially of oxidised polydimethylsiloxane and having a thickness from 10 to 30 nm, wherein said thickness is measured using time of flight secondary ion mass spectrometry, and upper layer (52) comprising substantially crosslinked polydimethylsiloxane and having a thickness less than 2 nm, said thickness measured by X-ray photoelectron spectroscopy. Present invention relates to a medical device for injection and to a method of producing lubricating coating.EFFECT: obtaining devices for injections, including medical container compatible with biotechnological preparations, which enables to avoid denaturation and/or aggregation of preparation after filling, wherein said devices have good sliding properties.21 cl, 14 dwg, 2 tblНастоящее изобретение относится к смазочному покрытию (5) для медицинского устройства для инъекций (1), включающему последовательно: нижний слой (50), находящийся в контакте с поверхностью (21) контейнера медицинского устройства, которую необходимо обеспечить смазкой, включающий смесь поперечно-сшитого и не поперечно-сшитого полидиметилсилоксана, промежуточный слой (51), состоящий в основном из окисленного полидиметилсилоксана и имеющий толщину, составляющую от 10 до 30 нм, где указанную толщину измеряют с помощью времяпролетной вторичной ионной масс-спектрометрии, и верхний слой (52), включающий по существу не поперечно-сшитый полидиметилсилоксан и имеющий толщину не более 2 нм, указанную толщину измеряют с помощью рентгеновской фотоэлектронной спектроскопии. Также настоящее изобретение относится к медицинскому устройству для инъекций и к способу получения смазочного покрытия