Provided is a functional patch for a pad, which is manufactured by mixing a functional particle, which is produced by mixing 40 to 70 wt % of a ferrite sintered body produced by mixing, granulating, and sintering 45 to 55 wt % of ferric oxide, 4 to 8 wt % of neodymium oxide, 12 to 16 wt % of zirconium oxide, 4 to 8 wt % of a silicon oxide-carbon composite, 4 to 6 wt % of copper oxide, 4 to 8 wt % of iron phosphate (FeP), 4 to 8 wt % of barium, and 2 to 4 wt % of magnesium with 30 to 60 wt % of zeolite including 10 to 20 wt % of zeolite A, 10 to 20 wt % of zeolite X, 10 to 20 wt % of zeolite L, 10 to 20 wt % of zeolite α, 10 to 20 wt % of zeolite β, and 10 to 20 wt % of silicalite-1 zeolite, with a binder, which is produced by polymerizing 30 to 60 mol % of an acrylonitrile polymerization unit, 5 to 30 mol % of an acrylamide polymerization unit, and 10 to 50 mol % of an acrylic acid or methacrylic acid-derived polymerization unit and mixing 10 to 30 parts by weight of polydopamine with respect to 100 parts by weight of a polymer, and then applying the same to a patch fabric.본 발명은 산화제2철 45~55 중량%, 산화네오디뮴 4~8 중량%, 산화지르코늄 12~16 중량%, 실리콘 산화물-탄소 복합체 4~8 중량%, 산화구리 4~6 중량%, 인화철(FeP) 4~8 중량%, 바륨 4~8 중량% 및 마그네슘 2~4 중량%를 혼합하여 과립화하고 소결시켜 제조된 페라이트 소결체 40~70 중량%； 및제올라이트A 10~20 중량%, 제올라이트X 10~20 중량%, 제올라이트L 10~20 중량%, 제올라이트α 10~20 중량%, 제올라이트β 10~20 중량%, 및 silicalite-1 제올라이트 10~20 중량%를 포함하는 제올라이트 30~60 중량%；를 혼합하여 제조된 기능성 입자를,아크릴로니트릴 중합 단위를 30 내지 60 몰%, 아크릴아미드 중합 단위를 5 내지 30 몰%, 아크릴산 또는 메타크릴산 유래 중합 단위를 10 내지 50 몰%를 중합시킨 후, 상기 중합체 100 중량부에 대하여 폴리도파민 10~30 중량부를 혼합시켜 제조된 바인더와 혼합하여 패치원단에 도포하여 제조되는 패드용 기능성 패치를 제공한다.