The The present invention cement composition kit for obtaining a bone cement composition and bone cement composition capable of forming a cured product having a high physical strength in practice necessary, together with having the biological activity performance to provide, as its object to provide a high mechanical strength and a method for manufacturing bone cement shaped article having a practically required to be, with the living body has a bow performance. Bone cement composition of the present invention is a median size measured by a laser diffraction / scattering type particle size distribution meter is 0.5 and 7.0 , BET specific surface area measured by the nitrogen adsorption method of 0.5 to 7.0 / g of titanium dioxide particles and , (meth) containing a component for the substrate formed by the acrylate-based polymer and a (meth) acrylate-based monomer, and characterized in that the content of the titanium dioxide particles is from 5 to 50% by weight based on the whole composition.본 발명은 생체 활성능을 가짐과 함께, 실용상 필요로 되는 높은 물리적 강도를 갖는 경화체를 형성할 수 있는 골시멘트 조성물 및 골시멘트 조성물을 얻기 위한 골시멘트 조성물 키트를 제공하는 것, 생체 활성능을 가짐과 함께, 실용상 필요로 되는 높은 물리적 강도를 갖는 골시멘트 성형체 및 그 제조 방법을 제공하는 것을 목적으로 한다. 본 발명의 골시멘트 조성물은, 레이저 회절/산란식 입도 분포계에 의해 측정되는 메디안 직경이 0.5 ∼ 7.0 ㎛ 이고, 질소 흡착법에 의해 측정되는 BET 비표면적이 0.5 ∼ 7.0 ㎡/g 인 이산화티탄 입자와, (메트)아크릴레이트계 폴리머 및 (메트)아크릴레이트계 모노머로 이루어지는 기재 형성용 성분을 함유하고, 상기 이산화티탄 입자의 함유 비율이 조성물 전체에 대해 5 ∼ 50 질량% 인 것을 특징으로 한다.