PROBLEM TO BE SOLVED: To produce a Nitinol material that is suitable for use in a human body or in other applications.SOLUTION: A fatigue-resistant Nitinol instrument has a working section in a deformed monoclinic martensitic state and an austenite finish temperature in the range of 40 to 60°C. Because the operating environment of the instrument is about 37°C, the working section remains in the monoclinic martensitic state during its use. The relatively high austenite finish temperature and fatigue resistance are achieved by subjecting the nickel-titanium alloy to a final thermal heat treatment in a temperature range of about 410 to 440°C while the nickel-titanium alloy is under constant strain of about 3 to 15 kg. Further, the high austenite finish temperature is achieved without subjecting the alloy to thermal cycling to produce shape memory. Additionally, there are no intermediate processing steps occurring between a step of obtaining a finished diameter of a wire or blank through cold processing and the final thermal heat treatment under constant strain.COPYRIGHT: (C)2015,JPO&INPIT【課題】人体又は他の用途に好適に使用可能なニチノール材料を製造することである。【解決手段】耐疲労性ニチノール器具は、変形単斜晶マルテンサイト状態にある作業部を備え、オーステナイト終了温度が40~60℃である。器具の使用環境が約37℃であるため、作業部はその使用中に単斜晶マルテンサイト状態を維持する。比較的高いオーステナイト終了温度及び耐疲労性は、ニッケル-チタン合金を約3~15kgの一定歪み下に置きつつ、ニッケル-チタン合金に約410~440℃の最終熱処理を施すことで得られる。また、高いオーステナイト終了温度は、形状記憶を得るための熱サイクルを合金に施すことなく得られる。更に、冷間加工によりワイヤー又はブランクの最終直径を得るステップと一定歪み下での最終熱処理との間に中間加工ステップが生じない。【選択図】図8