PROBLEM TO BE SOLVED: To provide a calcium phosphate-calcium sulfate composite that exhibits enhanced strength, excellent biocompatibility, superior osteoconductivity, and appropriate and adjustable bioresorption rate.SOLUTION: A bone cement formula has a powder component and a setting liquid component, wherein the powder component includes a calcium sulfate source and a calcium phosphate source with a weight ratio of the calcium sulfate source less than 65%, based on the total weight of the calcium sulfate source and the calcium phosphate source, and the setting liquid component comprises ammonium ion (NH4+) in a concentration of about 0.5 M to 4 M, wherein the calcium phosphate source includes tetracalcium phosphate (TTCP) and dicalcium phosphate in a molar ratio of TTCP to dicalcium phosphate of about 0.5 to about 2.5, and the calcium sulfate source is calcium sulfate hemihydrate (CSH), calcium sulfate dehydrate (CSD), or anhydrous calcium sulfate.COPYRIGHT: (C)2012,JPO&INPIT【課題】向上した強度、優れた生体適合性、高い骨伝導率、適切かつ調節可能な生体内吸収効率を示すリン酸カルシウム-硫酸カルシウム複合材の提供。【解決手段】粉成分および硬化液成分とを含む骨セメント材であって、前記粉成分が硫酸カルシウム源およびリン酸カルシウム源を含み、この際、前記硫酸カルシウム源の重量比が前記硫酸カルシウム源およびリン酸カルシウム源の合計重量に対して、65重量%未満であり、前記硬化液成分が約0.5M~4Mの濃度でアンモニウムイオン(NH4+)を含み、前記リン酸カルシウム源が、リン酸テトラカルシウム(TTCP)と第二リン酸カルシウムとを、含み、この際、第二リン酸カルシウムに対するTTCPのモル比が約0.5~約2.5であり、さらに前記硫酸カルシウム源が、硫酸カルシウム0.5水和物(CSH)、硫酸カルシウム2水和物(CSD)、または無水硫酸カルシウムである、骨セメント材。【選択図】なし