PROBLEM TO BE SOLVED: To provide a tape showing optically high thermoresponsiveness and the tape suitable for a medical tape.SOLUTION: The thermoresponsive polyurethane tape is made by reacting a polyester polyol having a melting point of 40 to 70°C and a number average molecular weight of 800 to 10,000 with a polyfunctional isocyanate having ≥3 functional groups to ensure that the ratio between the number of hydroxyl groups of the polyester polyol and the number of the isocyanate groups of the polyfunctional isocyanate will become 0.6 to 0.95, and is made of thermoresponsive polyurethane showing reversible thermoresponsiveness to optical transparency and the thermoresponsiveness of increasing the optical transparency when it is heated to a temperature equal to or higher than the melting point of the polyester polyol, or of reducing the optical transparency when it is cooled to less than the melting point.COPYRIGHT: (C)2013,JPO&INPIT【課題】光学的な面での優れた熱応答性を示すテープを提供し、医療用テープなどに適したテープを提供すること。【解決手段】融点が40~70℃で数平均分子量が800~10000のポリエステルポリオールと、3官能以上の多官能イソシアネートとが、前記ポリエステルポリオールの水酸基の数に対する前記多官能イソシアネートのイソシアネート基の数の比率が0.6~0.95となるように反応されてなり、光透過性に可逆的な熱応答性を示し、前記ポリエステルポリオールの融点以上の温度に加熱した際に光透過性が増大し、前記融点未満に冷却した際に光透過性が低下する前記熱応答性を示す熱応答性ポリウレタンからなることを特徴とする熱応答性ポリウレタンテープ等を提供する。【選択図】 なし