The invention relates to a porous zirconia article in particular for use in the dental or orthodontic field, the porous zirconia article comprising ZrO2: 80 to 87 wt.%,Y2O3: 3 to 5 wt.%, AI2O3: 10 to 14 wt.%, wt.% with respect to the weight of the porous zirconia article, the porous zirconia article being characterized by a BET surface from 15 to 100 m2/g. The invention also relates to a sintered zirconia article in particular for use in the dental or orthodontic field, the sintered zirconia article comprising ZrO2: 80 to 87 wt.%, Y2O3: 3 to 5 wt.%), AI2O3: 10 to 14 wt.%, wt.%) with respect to the weight of the porous zirconia article, the sintered zirconia article being characterized by a corundum crystal phase content of 7 to 12 wt.%>； and a flexural strength of at least 2,000 MPa.L'invention concerne un article poreux en zircone destiné en particulier à être utilisé dans le domaine dentaire ou orthodontique, l'article poreux en zircone consistant en ZrO2 : 80 à 87 % en poids, Y2O3 : 3 à 5 % en poids, Al2O3 : 10 à 14 % en poids, en % en poids par rapport au poids de l'article en zircone poreux, l'article en zircone poreux étant caractérisé par une surface BET de 15 à 100 m2/g. L'invention concerne également un article fritté en zircone destiné en particulier à être utilisé dans le domaine dentaire ou orthodontique, l'article fritté en zircone consistant en ZrO2 : 80 à 87 % en poids, Y2O3 : 3 à 5 % en poids, Al2O3 : 10 à 14 % en poids, en % en poids par rapport au poids de l'article en zircone poreux, l'article en zircone fritté étant caractérisé par une teneur en phase cristalline de corindon de 7 à 12 % en poids et une résistance à la flexion d'au moins 2 000 MPa.